高溫合金牌號和化學成分列表說明
- 2016-03-02 14:34:08
-
1)牌號和化學成分見表3-28、表3-29。
表8-28高溫合金的牌號及化學成分牌號化學成分(質量分數)(%)新牌號CCrNiWM0A1TiFeNbVBCeMnSiPS其他固溶強化型鐵基合金GHl015≤O.0819.0~22.O34.0~39.04.80~5.802.50~3.20余量1.10~1.60≤O.010≤0.050≤1.50≤0.60≤0.020≤O.015GHl0l6≤O.0819.0~22.O32.0~36.O5.00~6.002.60~3.30余量0.90~1.400.10~O.30≤0.010≤O.050≤1.80≤O.60≤O.020≤0.015N0.13~O.25GHl035O.06~0.1220.0~23.O35.0~40.O2.50~3.50≤O.50O.70~1.20余量1.20~1.70≤O.050≤O.70≤0.80≤0.030≤0.020GHl040≤O.1215.O~17.524.0~27.O5.50~7.O0余量1.00~2.000.50~1.00≤O.030≤O.020N0.10~O.20GHll3l≤O.1019.O~22.O25.0~30.O4.80~6.002.80~3.50余量O.70~1.30≤O.005≤1.20≤O.80≤O.020≤O.020N0.15~0.30GHll40O.06~0.1220.O~23.O35.O~40.O1.40~1.802.00~2.50O.20~O.60O.70~1.20余量一一≤0.050≤0.70≤O.80≤O.025≤O.015時效硬化型鐵基合金GH2018≤O.0618.0~21.O40.0~44.O1.80~2.203.70~4.30O.35O.751.80~2.20余量≤O.015≤O.020≤O.50≤O.60≤0.020≤0.015Zr《0.050GH20360.34~0.4011.5~13.57.O~9.01.10~1.40≤O.12余量O.25~0.501.25~1.557.50~9.50O.30~O.80≤0.035≤0.030GH2038≤0.10lO.O~12.518.0~21.O≤0.502.30~2.80余量≤O.008≤1.00≤1.00≤0.030≤O.020GH2130≤O.0812.O~16.O35.O~40.O5.00~6.501.40~2.202.40~3.20余量≤O.020≤0.020≤0.50≤0.60≤O.015≤O.015GH2132≤O.0813.5~16.O24.O~27.01.00~1.50≤0.401.75~2.30余量0.10~0.50O.00l~0.010≤2.00≤1.00≤O.030≤O.020GH2135≤O.0814.O~16.O33.0~36.01.70~2.201.70~2.202.00~2.802.10~2.50余量≤O.015≤0.030≤0.40≤0.50≤0.020≤O.020GH2136≤0.0613.O~16.024.5~28.51.0D~1.75≤O.352.403.20余量O.01~0.10O.005~O.025≤O.35≤O.75≤O.025≤O.025GH2302≤O.0812.O~16.O38.0~42.03.50~4.501.50~2.501.80~2.302.30~2.80余量≤O.OlO≤O.020≤0.60≤O.60≤0.020≤O.010Zr≤O.050牌號化學成分(質量分數)(%)新牌號CCrNiWM0AlTiFeNbVBCeMnSiPS其他固溶強化型鎳基合金GH3030≤O.1219.0~22.0余量≤0.150.15~O.35≤1.50≤0.70≤O.80≤0.030≤0.020GH3039≤O.0819.0~22.O余量1.80~2.30O.35~O.750.35~0.75≤3.OO.90~1.30≤O.40≤0.80≤O.020≤0.012GH3044≤0.1023.5~26.5余量13.0~16.0≤1.50≤0.500.30~0.70≤4.0≤O.50≤O.80≤0.013≤O.013GH3128≤O.0519.O~22.0余量7.5~9.O7.50~9.OO.40~0.800.40~O.80≤2.0≤O.005≤0.050≤0.50≤O.80≤O.013≤O.013Zr≤O.06時效硬化型鎳基合金GH4033O.03~O.0819.0~22.O余量O.60~1.002.40~2.80≤4.O≤0.010≤0.010≤0.35≤0.65≤O.015≤O.O07GH4037O.03~0.1013.O~16.0余量5.00.002.00~4.001.70~2.301.80~2.30≤5.00.10~0.50≤0.020≤0.020
- 上一篇 [返回首頁] [打印] [返回上頁] 下一篇